Process gas and method for laser welding

ABSTRACT

A process gas for use in laser welding with a laser beam focused onto the work piece to be welded. The inventive process gas comprises helium, nitrogen, and at least one of carbon dioxide in an amount of up to 40% by volume, and oxygen in an amount of up to 30% by volume. The gas may comprise not more than 85% by volume of helium. Also disclosed are methods of laser welding using the inventive process gas. The invention is suitable for laser welding of low-alloy steels and coated, especially zinc-coated steels.

[0001] The invention relates to a process gas for laser welding with a laser beam, focused on a workpiece to be welded. Furthermore, the invention relates to a method for laser welding, whereby a focused laser beam is guided to a workpiece surface to be machined, and an inert gas-containing process gas stream is guided against the workpiece surface, where the process gas is applied.

[0002] The properties of laser irradiation, in particular the intensity and good focusability, have resulted in the use of lasers today in many areas of material machining. The laser machining systems are well-known. They usually exhibit a laser machining head, optionally with a nozzle, arranged coaxially to the laser beam. Laser machining systems are often used in connection with a computerized numeric control (CNC).

[0003] A focused laser beam is understood to mean within the scope of the invention a laser beam, focused essentially on the workpiece surface. Besides the predominantly used method with laser irradiation, focused on the workpiece surface, the invention can also be applied to a rarely used variant with irradiation that is not focused exactly on the workpiece surface.

[0004] In many methods of laser material machining, metallic and/or other material is heated to temperatures at which a reaction with the enveloping gases takes place. Therefore, in many cases industrial gases are used in order to carry out material machining processes more effectively, faster and/or with improved quality.

[0005] EP 579 205 includes a process gas mixture for laser welding, which contains 5 to 35% oxygen in argon, nitrogen, or helium. In place of oxygen, dry air can also be used. In this respect the dry air content may not fall below 25%.

[0006] In laser welding the process gases fulfill various tasks. The control and reduction of the plasma is mandatory at high laser performances. This is known, for example, from the publication “Laser im Nebel”, Dr. W. Danzer and Klaus Behler, LASER journal, edition January 1987, pages 32 to 36. Other tasks, like the protection against oxidation, a metallurgical optimization and/or a maximization of the speed and quality (splatter, pores, weld quality), have been ignored to date.

[0007] In laser welding it is known to use inert protective gases, like helium or argon. Even nitrogen is used to some degree. Now and then carbon dioxide, oxygen or hydrogen are also mixed in with argon or nitrogen.

[0008] Therefore, the invention was based on the problem of providing a process gas and a corresponding method that enables an improved laser welding. In particular, besides the control and reduction of the plasma, protection against oxidation, metallurgical optimization and/or maximization of the speed and the quality are also achieved with the aid of the process gas.

[0009] The invention solves this problem in that the process gas contains between 5 and 50% by vol. helium and, besides nitrogen, at least carbon dioxide with a content of 1 to 40% by vol.

[0010] It is crucial for the invention that the process gas exhibit, besides an inert gas content, also an active gas content.

[0011] Tests have demonstrated that even just a relatively low helium content on the order of magnitude of about 25% by vol. (for example, ±10%) usually suffices for an effective plasma control. The exact percentage for the helium content depends on various factors, such as the laser power, the energy density, the type of material, the quantity of vaporized material, the quantity of protective gas, the type of gas feed to the welding process, etc. Against the background of these influencing factors, the adjustment of the gas composition does not present any problem to the ordinarily skilled in the field.

[0012] In an advantageous embodiment of the invention, the process gas contains, besides helium and nitrogen, carbon dioxide with a content of 1 to 40% by vol. and oxygen with a content of up to 30% by vol.

[0013] In a further embodiment of the invention, the process gas contains between 1 and 35% by vol. carbon dioxide, preferably between 5 and 30% by vol. carbon dioxide, especially preferred between 10 and 25% by vol. carbon dioxide.

[0014] Tests with zinc -coated sheets yielded very good results with a content ranging from 10 to 25% by vol. carbon dioxide (for example, 15% by vol. CO₂). The inventive carbon dioxide content resulted in significantly more constant welding results. The welding process was significantly safer and less sensitive to contamination of the weld region. The speed could be noticeably increased.

[0015] In a design variant the process gas contains oxygen with a content of more than 10% by vol. oxygen, preferably between 15 and 25% by vol. oxygen. The process gas of this embodiment provides in particular for a significant increase in the welding speed.

[0016] In another variant the process gas contains between 0.1 and 20% by vol. oxygen, preferably between 0.5 and 10% by vol. oxygen. In this design variant the aspect of the protection of the workpiece against oxidation is especially distinct.

[0017] In particular, process gases

[0018] comprising a ternary gas mixture with the components helium, nitrogen and carbon dioxide,

[0019] comprising a quaternary gas mixture with the components helium, nitrogen carbon dioxide, and oxygen,

[0020] comprising a quaternary gas mixture with the components helium, nitrogen, argon and carbon dioxide, or

[0021] comprising a ternary gas mixture with the components helium, nitrogen, argon, carbon dioxide and oxygen, have proved useful.

[0022] In an embodiment of the invention, in particular of the ternary, quaternary or quinary gas mixtures, process gases, which contain between 5 and 50% by vol. helium, 1 to 40% by vol. carbon dioxide, 0 to 40% by vol. oxygen, 0 to 40% by vol. (in particular 0 to 25% by vol., preferably 0 to 20% by vol., especially preferred 0 to 15% by vol.) argon and the rest nitrogen are suitable for laser welding.

[0023] In this respect helium serves to suppress or control the plasma, carbon dioxide assists the fusion and the addition of oxygen can induce several specific positive effects in the welding process and contribute to the increase in quality. Nitrogen as well as argon increase the shielding of the welding zone. Nitrogen and argon also fulfill at least partially the task of the helium and contribute, therefore, as an economical substitute for the inert gas helium, increasing the economic efficiency of laser welding.

[0024] The invention can be used in connection with all kinds of lasers. Above all, it is suitable for use in laser machining with Nd:YAG lasers, diode lasers and CO₂ lasers.

[0025] Low-alloyed steels and coated, in particular zinc-coated steels can be welded especially advantageously with the inventive process gas. 

1. Process gas for laser welding with a laser beam, focused on a workpiece to be welded, characterized in that the process gas contains between 5 and 50% by vol. helium and, besides nitrogen, at least carbon dioxide with a content of 1 to 40% by vol.
 2. Process gas, as claimed in claim 1, characterized in that the process gas contains, besides helium and nitrogen, carbon dioxide with a content from 1 to 40% by vol. and oxygen with a content of up to 30% by vol.
 3. Process gas, as claimed in claim 1 or 2, characterized in that the process gas contains between 1 and 35% by vol. carbon dioxide, preferably between 5 and 30% by vol. carbon dioxide.
 4. Process gas, as claimed in claim 2 or 3, characterized in that the process gas contains more than 10% by vol. oxygen, preferably between 15 and 25% by vol. oxygen.
 5. Process gas, as claimed in claim 2 or 3, characterized in that the process gas contains between 0.1 and 20% by vol. oxygen, preferably between 0.5 and 10% by vol. oxygen.
 6. Process gas, as claimed in any one of the claims 1 to 4, characterized in that the process gas comprises a ternary gas mixture with the components helium, nitrogen and carbon dioxide, quaternary gas mixture with the components helium, nitrogen, carbon dioxide, and oxygen, quaternary gas mixture with the components helium, nitrogen, argon and carbon dioxide, or quinary gas mixture with the components helium, nitrogen, argon, carbon dioxide and oxygen.
 7. Process gas, as claimed in any one of the claims 1 to 5, in particular as claimed in claim 6, characterized in that the process gas contains between 5 and 50% by vol. helium, 1 to 40% by vol. carbon dioxide, 0 to 40% by vol. oxygen, 0 to 40% by vol. argon and the rest nitrogen.
 8. Method for laser welding, whereby a focused laser beam is guided to a workpiece surface to be machined and an inert gas-containing process gas stream is guided against the workpiece surface, characterized in that a process gas, as claimed in any one of the claims 1 to 7, is used.
 9. Application of a process gas, as claimed in any one of the claims 1 to 8 for laser welding of low-alloyed steels and/or coated, in particular zinc-coated steels. 